Silicone Tin RTV
R-1320 Translucent (15A Shore)
R-1320 A/B Two-Part, Tin RTV (Condesation Cure) Translucent Silicone is a room temperature vulcanizing rubber intended primarily for making puppet skins and highly flexible parts that can be pigmented with Silicone pigments.
Features:
*Excellent Physical Properties with High Tear Resistance
*Low Viscosity for Ease of Pouring
*Flesh Skin Softness
*Fast Cure (3HR) Brush-On Catalyst R-1300TH SP B
| R-1320 A/B | Brush-On Catalyst R-1300TH SP B | Softner F-100 | |
| Color: | Translucent | Clear | Clear |
| Mix Ratio: | 100/10 | 100/10 | 10 to 200% |
| Mixed Viscosity: | 28,000 | Thixotropic | 50 |
| Specific Gravity: | 1.08 | 1.08 | 1 |
| HardnessA Shore: | 15 | 10 | Varies |
| Tensile Strength PSI: | 503 | * Gel- 30 min | NA |
| Elongation: | 605 | * Cure- 3 hours | NA |
| Tear Resistance: | 105 | NA | NA |
Mixing Instructions
R-1320 A/B is processed by adding the curing agent B. The addition of 10% catalyst (by weight) has a pot life of 45 minutes – 1 hour. Since material is clear, a double mix is recommended to ensure a thorough mix. Softening agent F-100 can be used to create a gel like silicone medium for movement or additional soft feeling. After the mold (or part) has been removed from the master, it should be left for 24 hours in order to develop its maximum mechanical strength.
The information and data contained herein are based on information we believe reliable. Each user of the material should thoroughly test any application and independently conclude satisfactory performance before commercializing. Suggestions of uses should not be taken as inducements to infringe on any particular patent.